Experimental Investigation of Crack Initiation in Face-Centered Cubic Materials in the High and Very High Cycle Fatigue Regime

Straub, Thomas

Abstract (englisch):
This book investigates the fatigue mechanisms and crack initiation of Ni, Al and Cu on a small-scale in the Very High Cycle Fatigue regime by means of innovative fatigue experimentation. A novel custom-built resonant fatigue setup showed that the sample resonant frequency changes with increasing cycle number due to fatigue damage. Mechanisms such as slip band formation have been observed. Cyclic hardening, vacancy and oxidation formation may be considered as early fatigue mechanisms.


Zugehörige Institution(en) am KIT Institut für Angewandte Materialien - Werkstoff- und Biomechanik (IAM-WBM)
Publikationstyp Hochschulschrift
Jahr 2016
Sprache Englisch
Identifikator DOI: 10.5445/KSP/1000051515
ISBN: 978-3-7315-0471-9
ISSN: 2192-9963
URN: urn:nbn:de:0072-515156
KITopen ID: 1000051515
HGF-Programm 43.22.01; LK 01
Verlag KIT Scientific Publishing, Karlsruhe
Umfang XXX, 185 S.
Serie Schriftenreihe des Instituts für Angewandte Materialien, Karlsruher Institut für Technologie ; 55
Abschlussart Dissertation
Fakultät Fakultät für Maschinenbau (MACH)
Institut Institut für Angewandte Materialien - Werkstoff- und Biomechanik (IAM-WBM)
Prüfungsdaten 09.12.2015
Referent/Betreuer Prof. O. Kraft
Schlagworte Rissinitiierung, kubisch flächenzentriert, Ermüdung, unendliche Lebensdauer crack initiation, face-centered cubic, very high cycle fatigue, infinite lifetime
Bestellung Die Veröffentlichung ist bei KIT Scientific Publishing erschienen.
Weitere Informationen sowie gegebenenfalls Bestellmöglichkeiten finden Sie hier.
KIT – Die Forschungsuniversität in der Helmholtz-Gemeinschaft KITopen Landing Page