Structural elucidation of the degradation mechanism of nickel-rich layered cathodes during high-voltage cycling

Lai, J.; Zhang, J.; Li, Z.; Xiao, Y.; Hua, W. 1; Wu, Z.; Chen, Y.; Zhong, Y.; Xiang, W.; Guo, X.
1 Institut für Angewandte Materialien (IAM), Karlsruher Institut für Technologie (KIT)

Abstract:

Phase transition occurring during cycling plays a fundamentally important role in the cycling performance of nickel-rich cathodes. Here, splitting of two O3 phases, rather than the often observed O1 phases in the conventional LiCoO$_{2}$ electrode, was discovered in LiNi$_{0.85}$Co$_{0.10}$Mn$_{0.05}$O$_{2}$ at a high-voltage region (>4.6 V). Such degradation could be mitigated via Al doping.


Verlagsausgabe §
DOI: 10.5445/IR/1000119618
Veröffentlicht am 25.11.2021
Originalveröffentlichung
DOI: 10.1039/d0cc00327a
Scopus
Zitationen: 23
Dimensions
Zitationen: 27
Cover der Publikation
Zugehörige Institution(en) am KIT Institut für Angewandte Materialien – Energiespeichersysteme (IAM-ESS)
Publikationstyp Zeitschriftenaufsatz
Publikationsjahr 2020
Sprache Englisch
Identifikator ISSN: 0009-241X, 0022-4936, 1359-7345, 1364-548X, 2050-5620, 2050-5639
KITopen-ID: 1000119618
HGF-Programm 37.01.15 (POF III, LK 01) Reaction and Degradation Mechanisms
Erschienen in Chemical communications
Verlag Royal Society of Chemistry (RSC)
Band 56
Heft 36
Seiten 4886-4889
Vorab online veröffentlicht am 23.03.2020
Nachgewiesen in Dimensions
Scopus
KIT – Die Forschungsuniversität in der Helmholtz-Gemeinschaft
KITopen Landing Page