Investigation of edge formation during the coating process of Li-ion battery electrodes

In this manuscript, a method to reduce superelevations of lateral edges in cross-web direction during slot die coating of shear-thinning slurries for Li-ion battery electrodes (LIB) was developed. Therefore, the impact of the inner slot die geometry on the edge elevations was investigated. These elevations of the coating could be almost eliminated by optimizing the flow profile at the outlet of the slot die by modification of the internal geometry. This adaption is an essential step in optimizing the coating quality of slot die coating for battery electrodes to significantly reduce coating edges and, hence, the resulting production reject during the coating step of the industrial roll-to-roll process. It was also shown that lateral edges of the coating can be influenced explicitly by process parameters such as volume flow and gap between slot die and substrate. This correlation has already been shown for other shear-thinning material systems in previous works, which is now confirmed for this material system. At the beginning, the influence of different internal geometries on the formation of the edge elevations was shown. Finally, for the shear-thinning electrode slurry used in this work, optimal dimensions of the previously determined inner geometry for the slot die outlet were found. ... mehrThe optimization was performed for a state-of-the-art electrode area capacity (approximately 2.2 mAh cm$^{-2}$). The results enable a significant reduction of defects and reject in the coating step of large-scale production of LIB electrodes in the future, adding to a more sustainable battery production.