Resonant STXM-CT on single wire extracted from Pt/Rh gauzes treated under ammonia oxidation conditions for 24 h
Das, Srashtasrita
1; Stuckelberger, Michael E. 2; Pottbacker, Jan; Jakobtorweihen, Sven; Schroer, Christian G.; Horn, Raimund; Sheppard, Thomas Lennon
3
1 Institut für Katalyseforschung und -technologie (IKFT), Karlsruher Institut für Technologie (KIT)
2 Deutsches Elektronen-Synchrotron (DESY)
3 Institut für Technische Chemie und Polymerchemie (ITCP), Karlsruher Institut für Technologie (KIT)
1; Stuckelberger, Michael E. 2; Pottbacker, Jan; Jakobtorweihen, Sven; Schroer, Christian G.; Horn, Raimund; Sheppard, Thomas Lennon
31 Institut für Katalyseforschung und -technologie (IKFT), Karlsruher Institut für Technologie (KIT)
2 Deutsches Elektronen-Synchrotron (DESY)
3 Institut für Technische Chemie und Polymerchemie (ITCP), Karlsruher Institut für Technologie (KIT)
Abstract:
This tomographic scanning transmission X-ray microscopy (STXM-CT) data was acquired at the P06 microprobe beamline of the PETRA III (Deutsches-Elektronen Synchrotron DESY, Hamburg). The sample measured during this experiment was a single wire extracted from the Pt/Rh gauzes aged under industrial ammonia oxidation conditions for 24 h of time on stream. A detailed description of the dataset can be found in the corresponding readme file and its associated publication.
| Zugehörige Institution(en) am KIT | Institut für Katalyseforschung und -technologie (IKFT) Institut für Technische Chemie und Polymerchemie (ITCP) |
| Publikationstyp | Forschungsdaten |
| Publikationsdatum | 22.02.2024 |
| Erstellungsdatum | 15.12.2020 - 21.12.2020 |
| Identifikator | DOI: 10.35097/1929 KITopen-ID: 1000168696 |
| Lizenz | Creative Commons Namensnennung 4.0 International |
| Liesmich | In this experiment, ex situ STXM-CT was performed on single wires, with angles ranging from 0 to 360 degrees. The single wires were extracted from aged Pt/Rh gauzes treated under industrial ammonia oxidation conditions for 24 h of reaction time. The data available here contains the final and processed tomographic volumes of the wire measured at two energies above and below the Rh K-edge, at 23300 eV and 23208 eV respectively. Each 3D volume has been stacked as slices in each TIFF file provided here. |
| Art der Forschungsdaten | Dataset |