Transformation induced plasticity (TRIP) due to precipitation during continuous tempering of quenched and tempered steels

Heat treatment is an essential step in achieving the desired characteristics in steels. Quenched and tempered
(Q&T) steels are often tempered to adjust the strength-ductility ratio by taking advantage of the precipitation
of carbides. In practice, many parts already contain residual stresses, for example due to the temperature
gradients during surface hardening, and therefore tempering takes place under the influence of these stresses.
The occurring transformation induced plasticity (TRIP) means significant plastic deformation during a phase
transformation under a stress below the material’s yield strength. In this work, tempering TRIP of three
different Q&T steels has been studied by means of dilatometry, hardness measurements, and scanning electron
microscopy. The heating rate, as well as the direction and level of applied stress, have been varied. The results
have proven the existence of TRIP strain during continuous tempering and its linear dependence on the fraction
of the precipitates. A higher amount of carbon results in a growth of the precipitates surface area percentage,
leading to an increase in the TRIP strain and consequently the TRIP constant. ... mehrThis indicates the presence of the
Greenwood–Johnson effect, which relates TRIP to the difference in volume between the existing and forming
phases.