Charpy impact properties of EUROFER97-3 after neutron irradiation at 330 °C and 540 °C to damage doses of 21–23 dpa
Chakin, Vladimir 1; Bonnekoh, Carsten
1; Gaisin, Ramil
1; Ziegler, Rainer 1; Duerrschnabel, Michael
1; Klimenkov, Michael
2; Gorr, Bronislava 2; Rieth, Michael
1
1 Institut für Angewandte Materialien – Angewandte Werkstoffphysik (IAM-AWP), Karlsruher Institut für Technologie (KIT)
2 Karlsruher Institut für Technologie (KIT)
1; Gaisin, Ramil
1; Ziegler, Rainer 1; Duerrschnabel, Michael
1; Klimenkov, Michael
2; Gorr, Bronislava 2; Rieth, Michael
11 Institut für Angewandte Materialien – Angewandte Werkstoffphysik (IAM-AWP), Karlsruher Institut für Technologie (KIT)
2 Karlsruher Institut für Technologie (KIT)
Abstract:
he reduced activation ferritic-martensitic (RAFM) EUROFER97-3 steel of two heat treatments (EUROFER97-3_1100/700 and EUROFER97-3_980/780) after irradiation in the BOR-60 fast reactor at temperatures of 330 °C and 540 °C, with damage doses ranging from 21.6 to 22.8 dpa showed big differences in the Charpy impact
properties depending on the irradiation temperature. Significant drop in the upper shelf energy (USE) and shift of the ductile-brittle transition temperature (DBTT) occurred after irradiation at 330 °C. However, irradiation at 540°C resulted in only minor changes in the USE and DBTT compared to the unirradiated reference state. Probably, these changes are attributed of the formation of radiation-induced defects and evolution in the phase structure.
properties depending on the irradiation temperature. Significant drop in the upper shelf energy (USE) and shift of the ductile-brittle transition temperature (DBTT) occurred after irradiation at 330 °C. However, irradiation at 540°C resulted in only minor changes in the USE and DBTT compared to the unirradiated reference state. Probably, these changes are attributed of the formation of radiation-induced defects and evolution in the phase structure.
| Zugehörige Institution(en) am KIT | Institut für Angewandte Materialien – Angewandte Werkstoffphysik (IAM-AWP) |
| Publikationstyp | Zeitschriftenaufsatz |
| Publikationsmonat/-jahr | 03.2026 |
| Sprache | Englisch |
| Identifikator | ISSN: 2352-1791 KITopen-ID: 1000190155 |
| HGF-Programm | 31.13.05 (POF IV, LK 01) Neutron-Resistant Structural Materials |
| Erschienen in | Nuclear Materials and Energy |
| Verlag | Elsevier |
| Band | 46 |
| Seiten | 102079 |
| Vorab online veröffentlicht am | 02.02.2026 |
| Schlagwörter | RAFM EUROFER97-3 steel; radiation hardening and embrittlement; neutron irradiation |